Thickness: 30micron to 50microns
Width: 1020mm, 1100mm, 1600mm, 1830mm, 1870mm, according to customer requirements
Fracture strength: longitudinal 40MPa ~ 60MPa Transverse 20MPa to 35MPa
Elongation at break: 150% ~ 275% lengthwise Transverse 200% ~ 300%
1）Good release film characteristics, convenient demoulding, and subsequent treatment
2）High transparency, easy to check artificial marble surface defects
3）The thickness difference is small and the flatness is high
4）Super wide, can meet the needs of various models in the market
5) Less additives, not easy to deteriorate, dry products can not produce oil
6) Water soluble films for mould release form a barrier between parts and mold surfaces that are still curing.
7) An ideal solution in the manufacturing of solid surface materials and engineered agglomerate stone for countertops, bathtubs, construction fascia, indoor flooring, etc.
8) PVA films for mould release are also resistant to solvents and yet water-soluble, they can also be customized to meet your specific processing needs.
The product is mainly used for demoulding artificial marble and as release film. In the production process of marble, the water-soluble film is placed inside the mold film to quickly demould.
A polyvinyl alcohol release film for artificial marble molding, which is a release film disposed between the original liquid and the shaping device when the original liquid which is a raw material of artificial marble is supplied to the shaping device and cured for molding, is characterized in that the release film is provided in the manufacturing of a wide range of artificial marble, and can suppress wrinkles, curls, and the like generated at both ends, and prevent the surface shape of the resulting artificial marble from being poor, The steps of grinding and grinding the artificial marble can be simplified.
Thickness: 30micron to 50microns.
Width: 1020mm, 1100mm, 1600mm, 1830mm, 1870mm, according to customer requirements.
Fracture strength: longitudinal 40MPa ~ 60MPa Transverse 20MPa to 35MPa.
Elongation at break: 150% ~ 275% lengthwise Transverse 200% ~ 300%.
Water dissolution time: ≤ 240 seconds, water temperature 25℃, standing in water, stirring can accelerate the dissolution.
Packing requirements: Roll and seal with polyethylene film separately, carton packing.
Storage conditions: dry, no direct solar radiation, no high temperature, no icing.